| Producer : | | pWPS-no. Producer : | |
| | | Examiner or examining body : | |
| | | WPQR-no. Producer : | |
| | | Date of welding : | |
| |
| Creation of the sweat connection | | welding sequence |
 | | |
| |
| material parameters |
| Welding process/es : | ISO 4063 - 135 | Metal active gas welding |
| Product type : | P | Plate |
| Execution of the weld : | BW | butt weld |
| Material group / parent metal (Bm1) : | 1.1 / EN 10025-2 - S235JR | Steels with a specified minimum yield strength ReH <= 275 N/mm2 |
| Thickness of material (Bm1) : | 3.0 mm | | - / - |
| Tube outside diameter (Bm1) : | - / - | | - / - |
| Material group / parent metal (Bm2) : | 1.1 / EN 10025-2 - S235JR | Steels with a specified minimum yield strength ReH <= 275 N/mm2 |
| Thickness of material (Bm2) : | 3.0 mm | | - / - |
| Tube outside diameter (Bm2) : | - / - | | - / - |
| Thickness of weld metal : | 3.0 mm | | - / - |
| welding position : | PC | horizontal position |
| Gouging/Backing : | ss nb | one-side welding welding with no backing |
| Sweat addition material (135) : | ISO 14341-A-G3Si1 | |
| Manufacturer's name (135) : | Carbofil 1 | OERLIKON |
| Sweat addition material () : | - / - | - / - |
| Manufacturer's name () : | - / - | |
| shielding gas (135) : | ISO 14175 - M21 - ArC - 18 / 12 l/min | Trade name: CORGON® 18 / Producer: Linde AG |
| shielding gas : | - / - | - / - |
| backing gas : | - / - | - / - |
| tungsten elektrode : | - / - | - / - |
| |
| technical parameter |
| Preheat time / preheating temperature : | - / - | - / - |
| redrying temperature : | - / - | - / - |
| interpass temperature : | - / - | - / - |
| cooling rate : | - / - | - / - |
| Information impulse welding |
| Basic volts / Pulse tension : | - / - | - / - |
| background current / Pulse stream : | - / - | - / - |
| |
| Comments: Dated lists of process parameters are provided in the WPS000364 listed |
| |
| | |
| | Max Mustermann |
| Place, Date of issue | | Stamp, Name and signature of examiner or of examining body |
| |
| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |