| Producer : |
|
pWPS-no. Producer : |
|
| |
|
Examiner or examining body : |
|
| |
|
WPQR-no. Producer : |
|
| |
|
Date of welding : |
|
| |
|
Creation of the sweat connection |
|
welding sequence |
|
|
|
|
| |
| material parameters |
| Welding process/es : |
ISO 4063 - 135 |
Metal active gas welding |
| Product type : |
P |
Plate |
| Execution of the weld : |
BW |
butt weld |
| Material group / parent metal (Bm1) : |
1.1 / EN 10025-2 - S235JR |
Steels with a specified minimum yield strength ReH <= 275 N/mm2 |
| Thickness of material (Bm1) : |
5.0 mm |
|
- / - |
| Tube outside diameter (Bm1) : |
- / - |
|
- / - |
| Material group / parent metal (Bm2) : |
1.1 / EN 10025-2 - S235JR |
Steels with a specified minimum yield strength ReH <= 275 N/mm2 |
| Thickness of material (Bm2) : |
5.0 mm |
|
- / - |
| Tube outside diameter (Bm2) : |
- / - |
|
- / - |
| Thickness of weld metal : |
5.0 mm |
|
- / - |
| welding position : |
PE |
overhead position |
| Gouging/Backing : |
ss nb |
one-side welding welding with no backing |
| Sweat addition material (135) : |
ISO 14341-A-G3Si1 |
|
| Manufacturer's name (135) : |
Carbofil 1 |
OERLIKON |
| Sweat addition material () : |
- / - |
- / - |
| Manufacturer's name () : |
- / - |
|
| shielding gas (135) : |
ISO 14175 - M21 - ArC - 18 / 12 l/min |
Trade name: CORGON® 18 / Producer: Linde AG |
| shielding gas : |
- / - |
- / - |
| backing gas : |
- / - |
- / - |
| tungsten elektrode : |
- / - |
- / - |
| |
| technical parameter |
| Preheat time / preheating temperature : |
- / - |
- / - |
| redrying temperature : |
- / - |
- / - |
| interpass temperature : |
- / - |
- / - |
| cooling rate : |
- / - |
- / - |
| Information impulse welding |
| Basic volts / Pulse tension : |
- / - |
- / - |
| background current / Pulse stream : |
- / - |
- / - |
| |
| Comments: Dated lists of process parameters are provided in the WPS000756 listed |
| |
|
|
|
|
|
|
Max Mustermann |
| Place, Date of issue |
|
Stamp, Name and signature of examiner or of examining body |
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|