S-ID: 00001  /  Mrs. Gabriele Musterfrau  |  P-ID: 000010  /  ISO 9606-2 141 P FW 22.3 S t5.0 PD sl

ISO 9606-2 141 P FW 22.3 S t5.0 PD sl
Test N° external:
DIN EN ISO 9606-2:2005-03
WPS related: 00100
Metallbau & Schmiedehandwerk GmbH

Test status

08/09/2025, G. Reuter
Werkskontrolle
QS Abteilung 98/15

08/09/2025



M. Mustermann



Check in writing



09/09/2025

1.00

M. Mustermann
 

11/09/2025


Dipl.-Ing. K. Prüfmann
 

12/09/2025


G. Reuter
 

19/11/2025

M. Mustermann

Dipl.-Ing. Klaus Prüfmann

00010/DE-12345-2025-11-19

Visual inspection: ISO 17637 / Assessment norm  (ISO 10042: B)


Number of samples: 1
Desired value (WPS)
t1  =  5.0 mm     t2  =  5.0 mm  
D1  =      D2  =   
a1  =  4.0 mm     a2  =   
Sample 1 z1 z2 a1 B C D h1 B C D
 Measuring point 1 5.8 6.0  4.1    ≥ 3.6     ≥ 3.2     ≥ 2.8    2.2    ≤ 2.3      ≤ 2.7    ≤ 4.0    
  z3 z4 a2       h2      
 Measuring point 2 5.7 5.9  4.0    ≥ 3.6     ≥ 3.2     ≥ 2.8    2.1    ≤ 2.3      ≤ 2.7    ≤ 3.9    
 
Sample 2 z1 z2 a1 B C D h1 B C D
 Measuring point 1   ≥ 3.6     ≥ 3.2     ≥ 2.8           
  z3 z4 a2       h2      
 Measuring point 2   ≥ 3.6     ≥ 3.2     ≥ 2.8           
 
Sample 3 z1 z2 a1 B C D h1 B C D
 Measuring point 1   ≥ 3.6     ≥ 3.2     ≥ 2.8           
  z3 z4 a2       h2      
 Measuring point 2   ≥ 3.6     ≥ 3.2     ≥ 2.8           
 
Sample 4 z1 z2 a1 B C D h1 B C D
 Measuring point 1   ≥ 3.6     ≥ 3.2     ≥ 2.8           
  z3 z4 a2       h2      
 Measuring point 2   ≥ 3.6     ≥ 3.2     ≥ 2.8           
No. DL / WL

0507 - linear misalignment

 		Y/N
X

0512 - excessive asymmetry of fillet weld (excessive unequal leg length)

 		Y/N
X

5011 - continuous undercut

 		Y/N
X

5012 - intermittent undercut

 		Y/N
X
   
 
  Assessment
a = accepted
na = not accepted
00010 / 01

  

X

  

  

   
 

a

  

  

  

  

   
 


  

  

  

  

   
 


  

  

  

  

   
 


  

  

  

  

   
 


  

  

  

  

   
 


  

  

  

  

   
 


  

  

  

  

   
 

Fracture test: ISO 9017 / Assessment norm (ISO 10042: B)

No. DL / WL position of
fracture

2011 - gas pore

 		Y/N
X

2012 - uniformly distributed porosity

 		Y/N
X

2016 - worm-hole

 		Y/N
X

0303 - oxide inclusion

 		Y/N
X

0401 - lack of fusion

 		Y/N
X

0402 - incomplete penetration (lack of penetration)

 		Y/N
X
   
 
  Assessment
a = accepted
na = not accepted
00010 / 01

X

  

  

  

  

  

   
 

a

  

  

  

  

  

  

   
 


  

  

  

  

  

  

   
 


  

  

  

  

  

  

   
 


  

  

  

  

  

  

   
 


  

  

  

  

  

  

   
 


  

  

  

  

  

  

   
 


  

  

  

  

  

  

   
 

other information